MATERIAL & PRODUCT CODE |
FORMULA |
MOL.
WEIGHT |
OXIDES
ENTERING
FUSION |
MOL.
WEIGHT OF
OXIDES |
CONVERSION FACTOR |
MELTING
POINT °C (M)
DECOMP.
POINT °C (D)
|
SPECIFIC
GRAVITY |
|
Alumina Calcined
100 mesh BA10
300 mesh BA20
|
Al2O3 |
101.9 |
Al2O3 |
101.9 |
1.0 |
M 2050 |
3.96 |
|
Alumina Hydrate BA30 |
Al2OH2O |
156 |
Al2O3 |
101.9 |
0.654 |
D 300 |
2.42 |
|
Antimony Oxide |
Sb2O3 |
291.5 |
Sb2O3 |
291.5 |
1.0 |
M 656 |
5.2 |
|
Barium Carbonate BA80
S6 |
BaCO3 |
197.4 |
BaO |
153.4 |
0.777 |
D 900
M 1360
|
4.29 |
|
Bone Ash
Natural BA150
Synthetic BA160
|
Ca3(PO4)2 |
310.3 |
CaO |
56.1 |
0.542 |
M 1670 |
3.2 |
|
Borax Fine BA130
S5
|
Na2O.2B3.O31OH2O |
381.5 |
Na2O
B2O3
|
62
69.6
|
0.162
0.365
|
D-IOH2O.200
M 741
|
1.73 |
|
Boric Acid
S5 |
B2O33H2O |
123.7 |
B2O3 |
69.6 |
0.563 |
D 185
M 577
|
1.49 |
|
Boro-Calcite |
2CaO.3B2O3.5H2O |
412 |
CaO
B2O3
|
56.1
69.6
|
0.271
0.51
|
|
2.95 |
|
Calcite-Omya 10 BA170 |
CaCO3 |
100.1 |
CaO |
56.1 |
0.561 |
D 825 |
2.71 |
|
China Clay |
Al2O3.2SiO2.2H2O |
258.1 |
Al2O3
SiO2
|
101.9
60.1
|
0.395
0.466
|
M 1770 |
2.62 |
|
China Clay (Calcined)
Eckalite 1 BA330
Eckaglas BA331
|
Al2O3.2SiO2 |
222 |
Al2O3
SiO2
|
101.9
60.1
|
0.46
0.54
|
M 1770 |
2.6 |
|
Chromium Oxide BA180 |
Cr2O3 |
152 |
Cr2O3 |
152 |
1.0 |
M1990 |
5.21 |
|
Cobalt Carbonate
BA220
S5
|
CoCO3 |
118.9 |
CoO |
74.9 |
0.631 |
D to Co3O4 |
|
|
Cobalt Oxide
(72% Cobalt)
BA230
|
Co3O4 |
240.8 |
CoO |
74.9 |
0.933 |
D to CoO 900 |
6.07 |
|
Copper Carbonate BA250 |
CuCO3 |
123.6 |
CuO |
79.6 |
0.645 |
D to CuO 200 |
3.6-4.0 |
|
Copper Oxide
Black BA260
|
CuO |
79.6 |
CuO |
79.6 |
1.0 |
M 1326 |
6.45 |
|
Cryolite |
Na3AIF6 |
210 |
Na2O |
62 |
0.443 |
M 1020 |
2.95 |
|
Dolomite
Natural BA310
Synthetic BA320
|
CaCO3MgCO3 |
184.4 |
CaO |
56.1 |
0.304 |
D 730-760 |
2.87 |
|
Feldspar Potash
(Premium Grade) BA350
|
K2O.Al2O3.6SiO2 |
556 |
K2O
Al2O3
SiO2
|
94.2
101.9
60.1
|
0.169
0.183
0.648
|
M 1250+ / - |
2.56 |
|
Feldspar Soda BA340 |
Na2O.Al2O3.6SiO2 |
524.3 |
Na2O
AlO3
SiO2
|
62
101.9
60.1
|
0.118
0.194
0.688
|
M 1250+ / - |
2.61 |